Rasps?
« on: July 01, 2018, 08:19:32 am »
So I have some old half round rasps that dont quite match up to the wood I use anymore. Are they any good as a forging material?
Logged

Offline bubby

  • Member
  • Posts: 11,054
Re: Rasps?
« Reply #1 on: July 01, 2018, 01:55:01 pm »
The best way to tell is to do a snap test on the tang
Logged
failure is an option, everyone fails, it's how you handle it that matters.
The few the proud the 27🏹

Offline Ryan Jacob

  • Member
  • Posts: 427
Re: Rasps?
« Reply #2 on: July 02, 2018, 04:11:17 am »
Snap test?
Logged

Offline bubby

  • Member
  • Posts: 11,054
Re: Rasps?
« Reply #3 on: July 02, 2018, 08:14:24 am »
Heat the tang to non magnetic and hold just a little longer, then quench in warm Canola oil. If it got hard when you hit it with a hammer it will snap off and not bend. If it bends heat it again and quench in water. If it won't snap now it won't harden
Logged
failure is an option, everyone fails, it's how you handle it that matters.
The few the proud the 27🏹

Offline Ryan Jacob

  • Member
  • Posts: 427
Re: Rasps?
« Reply #4 on: July 02, 2018, 09:37:30 am »
Can I do this with coals and a blower?
Logged

Offline bubby

  • Member
  • Posts: 11,054
Re: Rasps?
« Reply #5 on: July 02, 2018, 12:31:34 pm »
Yes you most certainly can
Logged
failure is an option, everyone fails, it's how you handle it that matters.
The few the proud the 27🏹

Offline Hawkdancer

  • Member
  • Posts: 5,027
Re: Rasps?
« Reply #6 on: July 02, 2018, 11:48:33 pm »
I'll throw in a question - don't  most of the Nicholson files make good forging material?  Of course, I guess it depends on what you want to forge (f)!
Hawkdancer
Logged
Life is far too serious to be taken that way!
Jerry

Offline bubby

  • Member
  • Posts: 11,054
Re: Rasps?
« Reply #7 on: July 03, 2018, 07:05:41 am »
Well it depends on what you want to build, if say you are building a knife snap test it. Strikers need to be hard too. Lots of newer files are just case hardened so I test them all
Logged
failure is an option, everyone fails, it's how you handle it that matters.
The few the proud the 27🏹

Offline Mesophilic

  • Member
  • Posts: 876
Re: Rasps?
« Reply #8 on: July 04, 2018, 03:43:13 pm »
Quote from: Hawkdancer on July 02, 2018, 11:48:33 pm
I'll throw in a question - don't  most of the Nicholson files make good forging material?  Of course, I guess it depends on what you want to forge (f)!
Hawkdancer

Old Nicholson USA files are great for making knives.  Keep an eye out for garage sales and scrap yards. The outta country ones you see on most store shelves are hit or miss.  There's alot of imports that are crappy steel that is just case hardened and won't make a knife.